Jalalian S, Emami Arjomand M, Mahavi A. Comparative Evaluation of Fracture Strength of Cusp Coverage with Composite Versus Unsupported Enamel Reinforced with Composite in Posterior Dental Restorations. J Res Dent Maxillofac Sci 2018; 3 (4) :26-32
URL: http://jrdms.dentaliau.ac.ir/article-1-215-fa.html
URL: http://jrdms.dentaliau.ac.ir/article-1-215-fa.html
Comparative Evaluation of Fracture Strength of Cusp Coverage with Composite Versus Unsupported Enamel Reinforced with Composite in Posterior Dental Restorations. . 1397; 3 (4) :26-32
چکیده: (3310 مشاهده)
Background and aim: Efficient bonding techniques should be employed for strengthening tooth structure. Whether to preserve intact dental tissue or to sacrifice some undermined parts can still be challenging. We aimed to evaluate the fracture strength of cusp coverage with composite versus unsupported enamel reinforced with composite in posterior restorations.
Materials and methods: In this in-vitro study, over-impressions were made from 36 sound human maxillary premolars using bleaching shields. The teeth were randomly divided into three groups (n=12): group 1) intact teeth, group 2) teeth with MOD cavities without cusp coverage, and group 3) teeth with MOD cavities and 1.5 mm of buccal and palatal cusp coverage. Wide MOD cavities were prepared such that only 1 mm of intact enamel was left unsupported at margins. The cavities were restored using light-cure glass ionomer and P60 composite using the over-impressions to achieve the normal tooth anatomy. The teeth were stored in water at 37°C for a week, and their fracture resistance was assessed using a universal testing machine. The load at fracture was recorded in Newton (N). Data were analyzed using one-way analysis of variance (ANOVA) and Tukey’s test with a 95% confidence interval (CI).
Results: The mean±standard deviation (SD) of fracture load was 1834.62±104.04 N in group 1, 750.34±147.46 N in group 2, and 1211.30±210.85 N in group 3. One-way ANOVA revealed significant differences between the groups (P=0.001). Likewise, Tukey’s test showed that the difference between the groups was statistically significant (P<0.05).
Conclusion: Using composite in restoring unsupported enamel must be combined with cusp coverage to increase fracture strength.
Materials and methods: In this in-vitro study, over-impressions were made from 36 sound human maxillary premolars using bleaching shields. The teeth were randomly divided into three groups (n=12): group 1) intact teeth, group 2) teeth with MOD cavities without cusp coverage, and group 3) teeth with MOD cavities and 1.5 mm of buccal and palatal cusp coverage. Wide MOD cavities were prepared such that only 1 mm of intact enamel was left unsupported at margins. The cavities were restored using light-cure glass ionomer and P60 composite using the over-impressions to achieve the normal tooth anatomy. The teeth were stored in water at 37°C for a week, and their fracture resistance was assessed using a universal testing machine. The load at fracture was recorded in Newton (N). Data were analyzed using one-way analysis of variance (ANOVA) and Tukey’s test with a 95% confidence interval (CI).
Results: The mean±standard deviation (SD) of fracture load was 1834.62±104.04 N in group 1, 750.34±147.46 N in group 2, and 1211.30±210.85 N in group 3. One-way ANOVA revealed significant differences between the groups (P=0.001). Likewise, Tukey’s test showed that the difference between the groups was statistically significant (P<0.05).
Conclusion: Using composite in restoring unsupported enamel must be combined with cusp coverage to increase fracture strength.
واژههای کلیدی: کامپازیت رزین .استحکام شکست . انله
نوع مطالعه: Original article |
موضوع مقاله:
Oral & maxillofacial surgery
| بازنشر اطلاعات | |
 |
این مقاله تحت شرایط Creative Commons Attribution-NonCommercial 4.0 International License قابل بازنشر است. |