Neshati A, Kouchak Dezfouli N, Sadafi M, Omidi S. Compressive Strength of Three Types of Heat-Cure Acrylic Resins: Acropars, Acrosun, and Meliodent. , J Res Dent Maxillofac Sci. 2021; 6 (4) :14-17
URL: http://jrdms.dentaliau.ac.ir/article-1-310-fa.html
URL: http://jrdms.dentaliau.ac.ir/article-1-310-fa.html
Compressive Strength of Three Types of Heat-Cure Acrylic Resins: Acropars, Acrosun, and Meliodent. , . 1400; 6 (4) :14-17
چکیده: (4758 مشاهده)
Background: Compressive strength of acrylic resin base is an effective factor on durability of a prosthesis. The purpose of this in vitro study was to compare the compressive strength of three different types of heat-cure acrylic resins.
Materials and Methods: In this in vitro experimental study, 60 acrylic samples were fabricated from Acropars, Acrosun, and Meliodent acrylic resins (n=20 from each). The specimens were placed in a universal testing machine and force was applied until their fracture. The load at fracture was recorded as the compressive strength. Data were analyzed using one-way ANOVA followed by the Tukey’s test.
Results: The mean compressive strength was 80.6 ± 6.9, 85.6 ± 6.9, and 71.9 ± 5.3 MPa for Acropars, Acrosun, and Meliodent, respectively. The compressive strength of Acrosun was significantly higher than that of other groups (P=0.047).
Conclusion: In general, the results showed that the highest and the lowest compressive strength values were related to Acrosun and Meliodent, respectively. These results indicated the optimal compressive strength of Iranian acrylic resins.
Materials and Methods: In this in vitro experimental study, 60 acrylic samples were fabricated from Acropars, Acrosun, and Meliodent acrylic resins (n=20 from each). The specimens were placed in a universal testing machine and force was applied until their fracture. The load at fracture was recorded as the compressive strength. Data were analyzed using one-way ANOVA followed by the Tukey’s test.
Results: The mean compressive strength was 80.6 ± 6.9, 85.6 ± 6.9, and 71.9 ± 5.3 MPa for Acropars, Acrosun, and Meliodent, respectively. The compressive strength of Acrosun was significantly higher than that of other groups (P=0.047).
Conclusion: In general, the results showed that the highest and the lowest compressive strength values were related to Acrosun and Meliodent, respectively. These results indicated the optimal compressive strength of Iranian acrylic resins.
نوع مطالعه: Original article |
موضوع مقاله:
Dental implant
| بازنشر اطلاعات | |
 |
این مقاله تحت شرایط Creative Commons Attribution-NonCommercial 4.0 International License قابل بازنشر است. |