[Home ] [Archive]    
:: Main :: About :: Current Issue :: Archive :: Search :: Submit :: Contact ::
Main Menu
Journal Information::
Articles archive::
For Authors::
For Reviewers::
Contact us::
Site Facilities::


Journal of Research in Dental & Maxillofacial Sciences is licensed under a "Creative Commons Attribution 4.0      

International (CC-BY 4.0)"      

Search in website

Advanced Search
Receive site information
Enter your Email in the following box to receive the site news and information.
Registered in




Search published articles

Showing 1 results for Salari

Gr Esfahani Zadeh, N Akhavan Saless, M Noor Bakhsh, Mh Salari, D Ghalebaaghi,
Volume 3, Issue 2 (Journal of Research in Dental & Maxillofacial Sciences Spring 2018)

Background and Aim: Due to the importance of the bond strength between zirconia core (ZC) and porcelain veneer (PV) as well as the paradox about the functionality of sandblasting on the solidity between those layers, this research aimed to evaluate the effect of sandblasting on the shear bond strength (SBS) between ZC and PV.
Materials and Methods: After preparing 20 zirconia discs (7 mm × 3 mm) in this experimental study, they were randomly divided into two groups of case and control. In the case group, sandblasting with 120-μm aluminum oxide particles (Al2O3) was performed under 3.5-bar pressure at 10 mm distance from the zirconia surface for 15 seconds. Next, all the samples were cleaned with ultrasonic and 96% isopropyl alcohol for 3 minutes as well as steam cleaning for 10 seconds. Then, the samples were veneered with porcelain (3 mm × 5 mm). SBS was assessed using a universal testing machine. After data collection, the mean and standard deviation (SD) were calculated and analyzed using T-test.
Results: The SBS between ZC and PV was 62.56±8.35 MPa in the case group (after sandblasting) and 94.62±7.69 MPa in the control group. The SBS showed a significant statistical difference between the two groups (P=0.001).
Conclusion: The result of this research indicated that sandblasting reduces the SBS between ZC and PV. Considering the limitations and the methodology of the study, the hypothesis regarding the positive impact of sandblasting on SBS was not proven.