Jalalian E, Bagheri M, Masoumi S. Effect of Core Thickness and Porcelain Sintering on Marginal Adaptation. J Res Dent Maxillofac Sci 2018; 3 (2) :1-6
URL: http://jrdms.dentaliau.ac.ir/article-1-195-fa.html
Effect of Core Thickness and Porcelain Sintering on Marginal Adaptation. . 1397; 3 (2) :1-6

URL: http://jrdms.dentaliau.ac.ir/article-1-195-fa.html


چکیده:   (3356 مشاهده)
Background and aim: Marginal adaptation affects the long-term success of full-coverage restorations. This study aimed to assess the effect of porcelain sintering and zirconia core thickness on the marginal adaptation of all-ceramic restorations.
Materials and methods: In this in-vitro experimental study, a standard brass die, 7 mm in length and 5 mm in diameter, was fabricated using a milling machine. A classic chamfer finish line with the depth of 0.8 mm was prepared with 10-degree tapered walls. Copings were fabricated on the die using the computer aided design/computer aided manufacturing (CAD/CAM) system and were divided into three groups (n=10) with 0.3-mm (group 1), 0.5-mm (group 2), and 0.7-mm (group 3) core thicknesses. The copings were placed on the dies and randomly coded. The vertical gap was measured at 10 points on the margin under a scanning electron microscope (SEM). After porcelain sintering, the crowns were placed again on the dies, and the vertical gap was measured again at the same points. Data were analyzed using analysis of variance (ANOVA) and paired t-test.
Results: There was a significant difference among the three groups in marginal gap (P<0.05). The comparison of marginal gaps before and after porcelain sintering showed no significant changes with 0.3-mm and 0.5-mm thicknesses (P>0.05) but the difference was statistically significant with 0.7-mm core thickness (P<0.05).
Conclusion: It may be concluded that by increasing the zirconia core thickness, the marginal gap of all-ceramic crowns decreases. Regarding 0.3-mm and 0.5-mm core thicknesses, porcelain sintering had no effect on marginal gap but regarding 0.7-mm core thickness, marginal gap increased after sintering.[U1] 

 [U1]5
واژه‌های کلیدی: Zirconia، CAD/CAM، Marginal fitness
متن کامل [PDF 275 kb]   (1333 دریافت)    
نوع مطالعه: Original article |

ارسال نظر درباره این مقاله : نام کاربری یا پست الکترونیک شما:
CAPTCHA

بازنشر اطلاعات
Creative Commons License این مقاله تحت شرایط Creative Commons Attribution-NonCommercial 4.0 International License قابل بازنشر است.

کلیه حقوق این وب سایت متعلق به می باشد.

طراحی و برنامه نویسی : یکتاوب افزار شرق

© 2024 CC BY-NC 4.0 | Journal of Research in Dental and Maxillofacial Sciences

Designed & Developed by : Yektaweb